PRODUCT DESCRIPTION LOCTITE EDAG 6017SS E&C provides the following product characteristics: Technology Thermoplastic Appearance Black Filler Type Carbon Cure Heat cure Operating TemperatureMaximum 100oC Product Benefits ● Screen printable ● Excellent screen residence time ● Flexible low temperature drying cycles ● Compatible with polyester film, paper and cardboard ● Good adhesion to polyester film Application Conductive Ink Typical Assembly Applications Various resistive applications, Printed resistors, Heating elements, Sensing devices and Protection against electrostatic discharge (ESD) Key Substrates Polyester LOCTITE EDAG 6017SS E&C screen printable ink is specifically designed for blending with EDAG PM 404 E&C to provide exceptional resistance in the production of low voltage circuitry on polyester film TYPICAL PROPERTIES OF UNCURED MATERIAL Solids Content by Weight, % 27 Viscosity, Brookfield , mPa·s (cP): Speed 20 rpm, @ 20oC 25,000 Density, , Kg/cm3 1,100 Shelf Life @ 5 to 30°C (from date of manufacture), year 1 Flash Point DIN 53213oC 78 TYPICAL SCREEN PRINTING PROCESS Emulsion Thickness Emulsion Thickness , μm 20 to 40 Recommended Squeegee Polyurethane , durometer 70 to 75 Recommended Screen Type Monofilament polyester screen, threads/cm 61 to 90 Stainless steel screen , threads/cm 77 to 110 Printing Equipment Type Manual Semi-automatic High speed reel-to-reel TYPICAL CURING PERFORMANCE Recommended Drying Conditions 5 to 10 minutes @ 120°C Blends of LOCTITE EDAG 6017SS E&C and Electrodag PM-404 can be dried in conventional air circulated ovens. Higher temperatures will shorten the drying time and will lead to more stable resistance values. For high speed production, jet drying, infra-red drying and drying in high speed reel-to-reel equipment can be used. The above cure profile is a guideline recommendation. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures. TYPICAL PROPERTIES OF CURED MATERIAL Physical Properties Coverage @ 10μm dry coating thickness, m2/kg wet product 12 Adhesion , grade 5B Electrical Properties Sheet Resistivity Blending ratios of LOCTITE EDAG 6017SS E&C and Electrodag PM-404, Dried 5 minutes @ 120oC, ohms/sq Electrodag 6017SS (% by weight) Electrodag PM-404 (% by weight) @ 25μm dry coating thickness 100 0 35 90 10 50 80 20 70 70 30 105 60 40 170 50 50 290 40 60 675 30 70 2160 25 75 4500 20 80 35,000 10 90 > 1e9 GENERAL INFORMATION For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS).